Đồ án tốt nghiệp - Synthesis and characterization of Epoxy/ Reduced graphene oxide CFASEFOHQTGTOTMT

Tên môn học: Khóa luận tốt nghiệp

Giá: 19.000đ

Tổng thanh toán:

19.000đ

Người đăng tải:

#10377

Chi tiết tài liệu :

Đồ án tốt nghiệp ngành Công nghệ vật liệu - Synthesis and characterization of Epoxy/ Reduced graphene oxide composites for anti static electricity: Faculty of high quality training Graduations thesis of the Materials technology - Trường Đại học Sư phạm Kỹ thuật Thành phố Hồ Chí Minh (HCMUTE)

Định dạng	PDF
Dung lượng	5.35 MB
Số trang	83
Ngành	Công nghệ vật liệu

Lượt xem	48
Ngày đăng	05/01/2026

HO CHI MINH CITY UNIVERSITY OF TECHNOLOGY AND EDUCATION

FACULTY OF APPLIED SCIENCES
DEPARTMENT OF MATERIALS TECHNOLOGY

BACHELOR THESIS
SYNTHESIS AND CHARACTERIZATION OF
EPOXY/REDUCED GRAPHENE OXIDE COMPOSITES FOR
C

SUPERVISOR:

Dr.Thanh-Truc Pham

STUDENT’S NAME:

Nguyen Quoc Thang

STUDENT’S ID NUMBER:

18130041

STUDENT’S NAME:

Nguyen Thi Thanh Truc

STUDENT’S ID NUMBER:

18130049

COURSE:

181300POLY

Ho Chi Minh City, August &amp 2022

HO CHI MINH CITY UNIVERSITY OF TECHNOLOGY AND EDUCATION

FACULTY OF APPLIED SCIENCES
DEPARTMENT OF MATERIALS TECHNOLOGY

BACHELOR THESIS
SYNTHESIS AND CHARACTERIZATION OF
EPOXY/REDUCED GRAPHENE OXIDE COMPOSITES FOR
ANTI STATIC ELECTRICITY
SUPERVISOR:

Dr.Thanh-Truc Pham

STUDENT’S NAME:

Nguyen Quoc Thang

STUDENT’S ID NUMBER:

18130041

STUDENT’S NAME:

Nguyen Thi Thanh Truc

STUDENT’S ID NUMBER:

18130049

COURSE:

181300POLY

Ho Chi Minh City, August &amp 2022

TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT TP. HCM

KHOA KHOA HỌC ỨNG DỤNG
BM CÔNG NGHỆ VẬT LIỆU

CỘNG HOÀ XÃ HỘI CHỦ NGHĨA VIỆT NAM
Độc lập - Tự do – Hạnh phúc

Tp. Hồ Chí Minh, ngày 25 tháng 02 năm 2022

NHIỆM VỤ KHÓA LUẬN TỐT NGHIỆP
Giảng viên hướng dẫn: TS. Phạm Thanh Trúc
Cơ quan công tác của giảng viên hướng dẫn: Trường Đại học Sư Phạm Kỹ thuật Thành phố Hồ Chí
Minh
Sinh viên thực hiện: 1. Nguyễn Thị Thanh Trúc
2. Nguyễn Quốc Thắng

MSSV: 18130049
MSSV: 18130041

1. Tên đề tài:
Tên đề tài tiếng Anh: Synthesis And Characterization Of Epoxy/Reduced Graphene Oxide
Composites For Anti Static Electricity
Tên đề tài tiếng Việt: Tổng hợp và khảo sát tính chất của Epoxy/rGO composite ứng dụng vào vật
liệu chống tĩnh điện.
2. Nội dung chính của khóa luận:
Tổng hợp thành công Graphene Oxide bằng phương pháp Hummers cải tiến.
Tổng hợp thành công vật liệu composite rGO/EP dựa trên phương pháp phối trộn solution mixing
Khảo sát tính chất cơ, tính chất điện của vật liệu composite và nhận xét về sự cải thiện tính chất khi
gia cường rGO.
Ứng dụng Composite vào chống tĩnh điện.,
3. Các sản phẩm dự kiến
Sản phẩm dạng thanh để khảo sát tính chất cơ.
Sản phẩm dạng tấm để khảo sát tính dẫn điện, kháng hóa chất.
Sản phẩm huyền phù để khảo sát sự phân tán.
4. Ngày giao đồ án:

.......................................................................................................................................
5. Ngày nộp đồ án:
.......................................................................................................................
...

...
posite
coatings: effect of deposition temperature on its surface morphology and
corrosion resistance,” RSC Adv., vol. 7, no. 49, pp. 31100–31109, 2017.
[39] Y. Xue, L. Zhu, H. Chen, J. Qu, and L. Dai, “Multiscale patterning of
graphene oxide and reduced graphene oxide for flexible supercapacitors,”
Carbon N. Y., vol. 92, pp. 305–310, 2015.
[40] I. R. S. Table, “Chart| Sigma-Aldrich.” 2021.
[41] G. B. Olowojoba et al., “A facile way to produce epoxy nanocomposites
having excellent thermal conductivity with low contents of reduced graphene
oxide,” J. Mater. Sci., vol. 52, no. 12, pp. 7323–7344, 2017.
[42] F. Iskandar, U. Hikmah, E. Stavila, and A. H. Aimon, “Microwave-assisted
reduction method under nitrogen atmosphere for synthesis and electrical
62

conductivity improvement of reduced graphene oxide (rGO),” RSC Adv., vol.
7, no. 83, pp. 52391–52397, 2017.
[43] K. K. H. De Silva, H.-H. Huang, R. Joshi, and M. Yoshimura, “Restoration of
the graphitic structure by defect repair during the thermal reduction of
graphene oxide,” Carbon N. Y., vol. 166, pp. 74–90, 2020.
[44] N. Domun, H. Hadavinia, T. Zhang, T. Sainsbury, G. H. Liaghat, and S.
Vahid, “Improving the fracture toughness and the strength of epoxy using
nanomaterials–a review of the current status,” Nanoscale, vol. 7, no. 23, pp.
10294–10329, 2015.
[45] K. Loamrat, M. Sappakittipakorn, P. Sukontasukkul, and N. Banthia, “Effect
of carbon fiber and graphite powder on resistivity of cement-based sensor
under compression,” Appl. Sci. Eng. Prog., vol. 7, no. 1, pp. 29–35, 2014.
[46] T. S. Sreeprasad and V. Berry, “How do the electrical properties of graphene
change with its functionalization?,” small, vol. 9, no. 3, pp. 341–350, 2013.
[47] M. Ashok Kumar, G. Ramachandra Reddy, Y. Siva Bharathi, S. Venkata
Naidu, and V. Naga Prasad Naidu, “Frictional coefficient, hardness, impact
strength, and chemical resistance of reinforced sisal-glass fiber epoxy hybrid
composites,” J. Compos. Mater., vol. 44, no. 26, pp. 3195–3202, 2010.
[48] M. R. Loos, L. A. F. Coelho, S. H. Pezzin, and S. C. Amico, “The effect of
acetone addition on the properties of epoxy,” Polímeros, vol. 18, pp. 76–80,
2008.

63

APPENDIX
Appendix 1: Raman spectroscopy

GO sample.

rGO (hydrazine) sample.

rGO (vitamin C) sample.
64

rGO (heat shock) sample.
Appendix 2: TGA diagram

EP/rGO composite sample.
Appendix 2: FTIR spectroscopy

EP/rGO (hydrazine) sample.

65

EP/rGO (vitamin C) sample.

Neat epoxy sample.

66