TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT THÀNH PHỐ HỒ CHÍ MINH
KHOA KHOA HỌC ỨNG DỤNG
BỘ MÔN CÔNG NGHỆ VẬT LIỆU

KHOÁ LUẬN TỐT NGHIỆP
NGHIÊN CỨU TÍNH CHẤT ỨC CHẾ VÀ HIỆP TRỢ ỨC
CHẾ ĂN MÒN CỦA HỢP CHẤT IMIDAZOLINE VÀ NANÔ
CURCUMIN CHO THÉP CACBON TRONG DUNG DỊCH
NaCl 3,5 wt.%

GVHD:
SVTH:
MSSV:
Khoá:

PGS. TS. NGUYỄN ĐĂNG NAM
LÊ VĂN TÀI
16130056
2016

Tp. Hồ Chí Minh, tháng 08 năm 2020

TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT THÀNH PHỐ HỒ CHÍ MINH
KHOA KHOA HỌC ỨNG DỤNG
BỘ MÔN CÔNG NGHỆ VẬT LIỆU

KHOÁ LUẬN TỐT NGHIỆP
NGHIÊN CỨU TÍNH CHẤT ỨC CHẾ VÀ HIỆP TRỢ ỨC
CHẾ ĂN MÒN CỦA HỢP CHẤT IMIDAZOLINE VÀ NANÔ
CURCUMIN CHO THÉP CACBON TRONG DUNG DỊCH
NaCl 3,5 wt.%

GVHD:
SVTH:
MSSV:
Khoá:

PGS. TS. NGUYỄN ĐĂNG NAM
LÊ VĂN TÀI
16130056
2016

Tp. Hồ Chí Minh, tháng 08 năm 2020

TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT
TP. HCM
KHOA KHOA HỌC ỨNG DỤNG
BM CÔNG NGHỆ VẬT LIỆU

CỘNG HOÀ XÃ HỘI CHỦ NGHĨA
VIỆT NAM
Độc lập - Tự do – Hạnh phúc

Tp. Hồ Chí Minh, ngày... tháng... năm 2020
NHIỆM VỤ KHÓA LUẬN TỐT NGHIỆP
Giảng viên hướng dẫn: PGS. TS. Nguyễn Đăng Nam
Cơ quan công tác của giảng viên hướng dẫn: Trường Đại học Duy Tân
Sinh viên thực hiện: Lê Văn Tài
MSSV: 16130056
1. Tên đề tài: Nghiên cứu tính chất ức chế và hiệp trợ ức chế ăn mòn của hợp chất
imidazoline và nanô curcumin cho thép cacbon trong dung dịch NaCl 3,5 wt.%
2. Nội dung chính của khóa luận: Tìm hiểu về thép cacbon, các ứng dụng, ăn mòn và
các phương pháp giảm thiểu ăn mòn trong dung dịch điện li Tìm hiểu về các phương
pháp điện hóa và phương pháp phân tích bề mặt trong nghiên cứu ăn mòn và giảm
thiểu ăn mòn Khảo sát ăn mòn của thép cacbon trong dung dịch NaCl 3,5 wt.% (giả
định nước biển) và hiệu suất ức chế ăn mòn của imidazoline với nồng độ 0, 500,
1000, 1500 và 2000 ppm và hiệu suất hiệp trợ ức chế của nanô curcumin với nồng
độ 0, 10, 50 và 100 ppm) Phân tích cơ chế ăn mòn, ức chế và hiệp trợ ức chế ăn
mòn Phân tích quá trình hình thành lớp màng bảo vệ hình thành trên bề mặt thép
sau khi sử dụng chất ức chế và hiệp trợ ức chế Và phân tích bề mặt của thép cacbon
trước và sau khi sử dụng chất ức chế và hiệp trợ ức chế để đảm bảo kết quả phân
tích điện hóa và cơ chế ăn mòn, ức chế và hiệp trợ ức chế được đề xuất.
3. Các sản phẩm dự kiến: 01 bộ kết quả và khóa luận tốt nghiệp
4. Ngày giao đồ án:
5. Ngày nộp đồ án:
6. Ngôn ngữ trình bày: Bản báo cáo: Tiếng Anh  
Tiếng Việt 
Trình bày bảo vệ: Tiếng Anh 
Tiếng Việt 

TRƯỞNG BỘ MÔN
(Ký, ghi rõ họ tên)

GIẢNG VIÊN HƯỚNG DẪN

PGS. TS. Nguyễn Đăng Nam
i

...

...
infrared
(FTIR) spectroscopy of biological tissues”. Appl. Spectrosc. Rev. 43, pp. 134179.
[60] M. Aziz, A. F. Ismail (2017). “X-Ray Photoelectron Spectroscopy (XPS)”.
Membrane Characterization, pp. 81–93.
[61] N. S. H. Vu, P. V. Hien, T. V. Man, V. T. Hanh Thu, M. D. Tri, N. D. Nam
(2018). “A study on corrosion inhibitor for mild steel in ethanol fuel
blend”. Materials. 11, pp. 59.

56

[62] N. D. Nam, V. Q. Thang, N. T. Hoai, P. V. Hien (2016). “Yttrium 3-(4nitrophenyl)-2-propenoate used as inhibitor against copper alloy corrosion in 0.1
M NaCl solution”. Corros. Sci. 112, pp. 451-461.
[63] N. S. Hoai Vu, P. V. Hien, M. Mathesh, V. T. Hanh Thu, N. D. Nam (2019).
“Improved corrosion resistance of steel in ethanol fuel blend by titania
nanoparticles and Aganonerion polymorphum leaf extract”. ACS omega. 4, pp.
146-158.
[64] P. V. Hien, N. S. H. Vu, V. T. H. Thu, A. Somers, N. D. Nam (2017). “Study of
yttrium 4-nitrocinnamate to promote surface interactions with AS1020 steel”.
Appl. Surf. Sci. 412, pp. 464-474.
[65] Y. J. Tan, S. Bailey, B. Kinsella (1996). “An investigation of the formation and
destruction of corrosion inhibitor films using electrochemical impedance
spectroscopy (EIS)”. Corros. Sci. 38, pp. 1545-1561.
[66] N. D. Nam, P. V. Hien, N. T. Hoai, &amp V. T. H. Thu (2018). “A study on the mixed
corrosion inhibitor with a dominant cathodic inhibitor for mild steel in aqueous
chloride solution”. J. Taiwan Inst. Chem. Eng. 91, pp. 556-569.
[67] E. Barsoukov, J. R. Macdonald (2005). “Impedance Spectroscopy Theory,
Experiment, and Applications, 2nd ed”. John Wiley &ampSons, Inc.
[68] J. R. Scully, D. C. Silverman, M. W. Kendig (1993). “Electrochemical
impedance: analysis and interpretation”. Philadelphia: American Society for
Testing and Materials, pp. 1-10.
[69] N. D. Nam, J. G. Kim (2010). “Effect of niobium on the corrosion behaviour of
low alloy steel in sulfuric acid solution”. Corros. Sci. 52, pp. 3377-3384.
[70] Z. Sanaei, M. Ramezanzadeh, G. Bahlakeh, B. Ramezanzadeh (2019). “Use of
Rosa canina fruit extract as a green corrosion inhibitor for mild steel in 1 M HCl
solution: A complementary experimental, molecular dynamics and quantum
mechanics investigation”. J. Ind. Eng. Chem. 69, pp. 18-31.
[71] D. Wahyuningrum, S. Achmad, Y. M. Syah, B. Buchari, B. Ariwahjoedi (2008).
“The synthesis of imidazoline derivative compounds as corrosion inhibitor
towards carbon steel in 1% NaCl solution”. J. Math. Fundam. Sci. 40, pp. 33-48.

57