Đồ án tốt nghiệp - Nghiên cứu độ bền mỏi của chi tiết dạng trục khi được chế tạo bằng phương PI 3 KL

TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT THÀNH PHỐ HỒ CHÍ MINH
KHOA CƠ KHÍ CHẾ TẠO MÁY
BỘ MÔN CÔNG NGHỆ CHẾ TẠO MÁY
***********

ĐỒ ÁN TỐT NGHIỆP
NGHIÊN CỨU ĐỘ BỀN MỎI CỦA CHI TIẾT DẠNG
TRỤC KHI ĐƯỢC CHẾ TẠO BẰNG PHƯƠNG PHÁP
IN 3D KIM LOẠI

GVHD:

PGS. TS PHẠM SƠN MINH

SVTH:

NGUYỄN TIẾN ĐẠT

MSSV:

20144072

Khóa :

2020-2024

Tp.Hồ Chí Minh, Tháng 7 2024

TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT THÀNH PHỐ HỒ CHÍ MINH
KHOA CƠ KHÍ CHẾ TẠO MÁY
BỘ MÔN CÔNG NGHỆ CHẾ TẠO MÁY
_______________________

ĐỒ ÁN TỐT NGHIỆP
NGHIÊN CỨU ĐỘ BỀN MỎI CỦA CHI TIẾT DẠNG
TRỤC KHI ĐƯỢC CHẾ TẠO BẰNG PHƯƠNG PHÁP
IN 3D KIM LOẠI

GVHD:

PGS. TS PHẠM SƠN MINH

SVTH: NGUYỄN TIẾN ĐẠT
MSSV:

20144072

Khóa: 2020 – 2024

Tp.Hồ Chí Minh, tháng 7 năm 2024

TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ
THUẬT THÀNH PHỐ HỒ CHÍ MINH
KHOA CƠ KHÍ CHẾ TẠO MÁY

CỘNG HÒA XÃ HỘI CHỦ NGHĨA VIỆT NAM
Độc lập – Tự do – Hạnh phúc

NHIỆM VỤ ĐỒ ÁN TỐT NGHIỆP
Học kỳ 2/Năm học 2023-2024
Giảng viên hướng dẫn:

PGS. TS. Phạm Sơn Minh

Sinh viên thực hiện:

Nguyễn Tiến Đạt MSSV: 20144072 Điện thoại: 0378428124

1. Mã số đề tài: CKM-116
-Tên đề tài: Nghiên cứu độ bền mỏi của chi tiết dạng trục khi được chế tạo bằng
phương pháp in 3D kim loại
2. Các số liệu, tài liệu ban đầu:
- Cơ sở LT về 3D kim loại
- Tài liệu về Nguyên lí – Chi tiết máy
- Tài liệu về độ bền mỏi và các mô hình kiểm tra độ bền mỏi
3. Nội dung chính của đồ :
- Cơ sở lý thuyết về CN in 3D
- Cơ sở LT về độ bền mỏi của chi tiết
- Chế tạo mẫu thử độ bền mỏi
- Kiểm tra độ bền mỏi của các mẫu
- Thống kê dữ liệu và viết báo cáo
4. Sản phẩm dự kiến:
- Báo cáo
- Các mẫu thử nghiệm
5. Ngày giao đồ án: 19/02/2024
6. Ngày nộp đồ án: 03/07/2024
7. Ngôn ngữ trình bày:
Bản báo cáo:
English  Vietnamese 
Trình bày bảo vệ:
TRƯỞNG BỘ MÔN
(Ký, ghi rõ họ tên)

English 

Vietnamese 
GIẢNG VIÊN HƯỚNG DẪN
(Ký, ghi rõ họ tên)

 Được phép bảo vệ: ……………………………..…. (GVHD ký, ghi rõ họ tên)

LỜI CAM ĐOAN
Tôi xin khẳng định rằng bài luận văn tốt nghiệp này là kết quả làm việc nghiêm túc
và trung thực của tôi là Nguyễn Tiến Đạt. Nội dung và thành phẩm trong luận văn
đều là thành quả từ sự nỗ lực không ngừng nghỉ của chúng tôi. Từ những chỉ dẫn
chu đáo và đóng góp hết sức quý báu từ PGS. TS. Phạm Sơn Minh, tôi đã hoàn
thành bài luận văn này dựa trên năng lực và sự cố gắng của chính mình, không lấy
cắp từ công trình nghiên cứu hay bài viết nào khác.

Tp.Hồ Chí Minh, tháng 7 năm 2024
Tác giả thực hiên đề tài

Nguyễn Tiến Đạt

CỘNG HÒA XÃ HỘI CHỦ NGHĨA VIỆT
NAM
Độc lập – Tự do – Hạnh
...

...
ess and Exposition, Tampa, FL, USA, 3–9 November 2017 (Vol. 14, p.
V014T07A004).
[6] Ziemian, C., Sharma, M., &amp Ziemian, S. (2012). Anisotropic mechanical properties
of ABS parts fabricated by fused deposition modelling. In M. Gokcek (Ed.), Mechanical
Engineering (pp. 159-180). InTech.
[7] Bagsik, A., &amp Schöppner, V. (2011). Mechanical properties of Fused Deposition
Modeling parts manufactured with Ultem*9085. In Proceedings of the Society of
Plastics Engineers ANTEC Conference (Anaheim), Boston, MA, USA, 8–10 May, 2011
(pp. 1-5).

76

[8] Chacón, J. M., Caminero, M. A., García-Plaza, E., &amp Núñez, P. J. (2017). Additive
manufacturing of PLA structures using fused deposition modelling: Effect of process
parameters on mechanical properties and their optimal ion. Materials &amp Design,
124, 143-157.
[9] Onwubolu, G. C., &amp Rayegani, F. (2014). Characterization and optimization of
mechanical properties of ABS parts manufactured by the fused deposition modelling
process. International Journal of Manufacturing Engineering, 2014, 1-13.
[10] Wu, W., Geng, P., Li, G., Zhao, D., Zhang, H., &amp Zhao, J. (2015). Influence of
layer thickness and raster angle on the mechanical properties of 3D-printed PEEK and a
scomparative mechanical study between PEEK and ABS. Materials, 8(9), 5834-5846.
[11] Ian Gibson, David Rosen, Brent Stucker, Mahyar Khorasani (2015), Additive
Manufacturing Technologies, Springer.
[12] Anamika Prasad, Shakti S. Gupta, R.K. Tyagi, Advances in Engineering Design
(2018), Springer.
[13] D. L. Olson, Gas-Metal Arc Welding, Welding, Brazing, and Soldering, ASM
hanbook, vol. 6, pp. 180-185, 1993
[14] L. V. Thảo, A preliminary study on gas metal arc welding-based additive
manufacturing of metal parts, Science and Tecnology Development Journal, vol.23, pp.
422-429, 2020.
[15] N. M. V Gunaraj, Application of response surface methodology for predicting weld
bead quality in submerged arc welding of pipes, Journal of Materials Processing
Technology, vol. 88, no. 1–3, pp. 266-275, 1999.

77

BẢNG THAM KHẢO
[1] Oxygen in Steel WMD after Welding with Micro-Jet Cooling.
[2] Study of Shielded Gases for MIG Welding.
[3] Influence of shielding gases in the welding of metals.
[4] Welding method for high crack sensitivity of Q&ampT steel.
[5] Study of Mechanical Behavious and Characterization of a Steel Joints in MIG
Welding under Varying Fluxes.
[6] MIG Welding parameter setting and guidelines.
[7] Electrode Reactions in Metal Finishing.

78